"World's Best Manufacturing Process with a continuous Production line for Sandwich PU/PIR Sandwich Panels."
Metal-faced polyurethane sandwich panels are the system of choice today for large industrial buildings refrigerated warehouses,
office blocks, exhibition halls, fair pavilions, schools, and sports halls. The aluminum or steel facings themselves are surface coated and can be manufactured with profiles of various depths
leading to a higher load-bearing capacity.
Polyurethane sandwich panels come complete with specially formed tongue-and-groove joints ensuring a perfect fit and
maximum integrity, Assembly is fast, easy, and cost-effective. As a result, these thin, relatively lightweight sandwich panels
can safely bridge wide spans.
The top and bottom coil (sheet metal) are clamped onto the plants unwinding unit and fed into the machine. In the first step, “corona system” cleans both reverse sides of the sheet metal using high frequency to remove greases and dirt and to guarantee the best possible subsequent full spread adhesion between foam and sheet metal. Thereafter the protective films are rolled onto outside of both metal sheets. The sheets are then brought together, the bottom sheet is foamed by the swinging foam head and the top sheet is mechanically steadied. Immediately after that, the panel is fed into the heated drying tunnel where the foam expands to its full volume, binds to the sheets and transforms both sheets to one robust, shear resistant composite structural panel. After leaving the tunnel the panels are cut according to your specification using flying saw/cutter.
Panel thickness available | 30mm, 40mm, 50mm, 60mm, 80mm, 100mm, 120mm |
Panel width available | 1060mm |
Panel length available | 2000mm-12000mm |
Average density | 40 ± 2kg/m |
Thermal conductivity | 0.024-0.03 W/m |
Temperature range | -40+800C |
Free from CFC | CFC free |
Type of foam | B3 |
Heat transfer co-efficient | -0.022W/M2*k |
Pressure | 0.10Mpa |
Cubic Area Change | =1%(-30 C – 100 C/96h) |
With 80 mm thick sandwich panels with polyurethane rigid foam, the U value is 0.297 W/(m K). In comparison, a solid wall with 24 cm thick masonry and 2 cm plaster walls has a U value of 1.85 W/(m K).
Rigid polyurethane foam combines excellent thermal insulation properties with good mechanical strength, making it an outstanding construction material that does not rot, mold-resistant, odorless and non-toxic for all conceivable applications, the foam is resistant to the chemicals typically used in construction and is compatible with most solvent-containing adhesives, paints and wood preservatives. Polyurethane rigid foam is extremely durable and can be installed easily and securely, ensuring cost-effective, efficient construction.
Puff (0.5/0.4) steel panel | 550 Mpa | |||||||
---|---|---|---|---|---|---|---|---|
puff thick (mm) | Weight kg/m2 | Area cm2 | Ix& cm4 | ZX-Top cm3 | ZX-Bottom cm3 | Ma (top) Kn.m | Ma (bottom) Kn.m | |
30.00 | 8.38 | 10.67 | 51.13 | 11.19 | 21.48 | 4.061 | 7.798 | |
40.00 | 8.42 | 10.72 | 73.52 | 14.76 | 24.75 | 5.359 | 8.986 | |
50.00 | 8.50 | 10.83 | 101.10 | 18.76 | 28.40 | 6.809 | 10.309 | |
fy= | 55 Kn/cm2 | |||||||
E= | 2.00E+08 KN/M2 |